Active Play AS C II is a polyether prepolymer based on polymeric MDI with high functionality (>2.5). The product is a one-component polyurethane adhesive appearing as a clear, amber liquid. It is characterized by viscosity of 1000-3000 mPas at temp. 25°C, with the content of NCO groups between 10.0-12.5%.
Active Play AS C II is a raw material dedicated to the production of cold and hot molded elements from SBR rubber granules obtained also in the process of recycling.
Active Play AS C II is a prepolymer dedicated to bonding black SBR granules also obtained from recycling of ground, used car tires.
SBR granules are obtained by cutting car tires. It is characterized by its black color, high abrasion and weather resistance. It dampens sound brilliantly, it is safe, flexible and does not absorb water. As a result, it is used in sports and leisure construction for the production of safe surfaces.
The pigmented prepolymer - Active Play AS C III - must be mixed before application. The SBR granules should be moistened with prepolymer and then placed in the mold so that it is cured under the influence of temperature and moisture while the press operates.
The properties of the molded part (such as a plate) depend on the size and the composition of the rubber granules, and quantity of the one-component polyurethane adhesive and in the case of the molded process, it also depends on the degree of compression during curing. The adhesive curing process takes place at temperatures from 70°C to 150°C. The choice of temperature and humidity depends on the applied technology and allows, among other things to reduce the time of curing/polymerization.
The prepolymer, combined with SBR granules, forms a good rigid joint preserving its elasticity at the same time. It contains no harmful organic solvents.
Active Play AS C II is designed for the production of SBR granules, particularly for the production of weights and similar products.
Advantages of product application:
easy to apply adhesive for joining rubber granules,
high resistance to temperature - in production of formable elements temperatures in the range from 70°C to 150°C can be applied,
higher humidity and temperature allows shortening of the hardening process of a surface or element.
Prepolymer based on diphenylmethane diisocyanate (MDI), Prepolymer based on diphenylmethane diisocyanate (MDI)
Manufacturer: PCC Rokita SA
PCC Rokita SA is one of the largest chemical companies in Poland as well as Central and Eastern Europe. Its activity includes the production of chloroalkali, polyether polyols, polyalkylene glycols and phosphorus derivatives.
All the above information related to the product are provided according to the best knowledge of the manufacturer and published in good faith. However, the manufacturer does not guarantee the information and contents of this document are complete and accurate, and shall not be liable for the results of using them. The user is obliged to verify and confirm the information and contents of this documentation on his/her own. The manufacturer reserves the right to change the content of this document at any time without stating reasons of such changes.
ISO 14001 
ISO 50001 
ISO 9001 
ISO 45001 